VSR60 Resistive to high pressure steam applications - Silicone Rubber Products

Special Grades - Product Code: VSR60 Resistive to high pressure steam applications
A very high quality compound, developed specifically to resist high pressure steam applications.
	Shore Hardness:	60° +/- 5°
	Elongation at break:	340%
	Tensile Strength:	7.5 N/mm
	Tear Strength:	11 N/mm
	Specific Gravity:	1.15
	Temperature Range:	-70°C to + 200°C
	Compression Set:	35%

Steam ageing at 140°C for 7 days	Hardness 61	Tensile strength MPa 5.0	Elongation to Break % 170	!00% Modulus MPa 2.83
Steam ageing at 140°C for 15 days	Hardness 62	Tensile strength MPa 5.1	Elongation to Break % 180	!00% Modulus MPa 23.06
Steam ageing at 140°C for 30 days	Hardness 63	Tensile strength MPa 4.4	Elongation to Break % 160	!00% Modulus MPa 2.78
Steam ageing at 140°C for 44 days	Hardness 60	Tensile strength MPa 4.4	Elongation to Break % 160	!00% Modulus MPa 2.45
Steam ageing at 140°C for 60 days	Hardness 62	Tensile strength MPa 4.1	Elongation to Break % 165	!00% Modulus MPa 2.91
Steam ageing at 160°C for 3 days	Hardness 60	Tensile strength MPa 5.8	Elongation to Break % 200	!00% Modulus MPa 3.16
Steam ageing at 160°C for 10 days	Hardness 58	Tensile strength MPa 4.2	Elongation to Break % 160	!00% Modulus MPa 2.64
Steam ageing at 160°C for 15 days	Hardness 59	Tensile strength MPa 4.5	Elongation to Break % 150	!00% Modulus MPa 2.79
Steam ageing at 160°C for 20 days	Hardness 60	Tensile strength Mpa 4.0	Elongation to Break % 160	!00% Modulus MPa 2.75
Steam ageing at 160°C for 25 days	Hardness 59	Tensile strength MPa 3.9	Elongation to Break % 170	!00% Modulus MPa 2.45
Steam ageing at 160°C for 30 days	Hardness 57	Tensile strength MPa 3.2	Elongation to Break % 140	!00% Modulus MPa 2.50
Steam ageing at 180°C for 1 day	Hardness 60	Tensile strength MPa 5.2	Elongation to Break % 200	!00% Modulus MPa 2.44
Steam ageing at 180°C for 3 days	Hardness 58	Tensile strength MPa 4.6	Elongation to Break % 170	!00% Modulus MPa 2.56
Steam ageing at 180°C for 4 days	Hardness 56	Tensile strength MPa 3.4	Elongation to Break % 150	!00% Modulus MPa 2.31
Steam ageing at 180°C for 7 days	Hardness 54	Tensile strength MPa 3.1	Elongation to Break % 140	!00% Modulus MPa 2.15
Steam ageing at 180°C for 10 days	Hardness 51	Tensile strength MPa 2.1	Elongation to Break % 120	!00% Modulus MPa 2.02

Special Grades - Product Code: VSR60 Resistive to high pressure steam applications